high chromium cast iron microstructure
Chromium Cast Iron by Manganese Alloying - CRTI Library
high-chromium cast iron is not commercially viable; a heat treatment is beneficial to the change of the microstructure. A mixture of martensite and residual
Learn MoreAbrasion Wear Resistance of Ni - Mo Alloyed High-Chromium
The paper presents the results of research on the high-chromium cast irons of chemical composition (in wt. %) 2-4 C, 21-22 Cr, 1-2 Mo, 5-6 Ni,
Learn MoreMicrostructural effect and wear performance of high chromium
2021. 7. 15. · High chromium white cast irons are ferrous alloys with chromium contents of 11 to 30 wt% and 1.8 to 3.6 wt% carbon . Elements such as Molybdenum, Nickel Fig. 1a and Fig. 1b
Learn MoreMicrostructure and properties of modified as‐cast hypereutectic high chromium cast iron
2022. 2. 17. · The present work studied the effects of different modification treatments on the microstructure and mechanical properties of hypereutectic high chromium cast iron containing about 35 wt% chromium and 4.0 wt% carbon. It was found that the primary carbides in the hypereutectic high chromium cast iron were all refined to different levels after different
Learn MoreMicrostructure and Sliding Wear Behavior of High
2022. 2. 10. · To improve the wear resistance of the low carbon steel (LCS), high chromium cast iron (HCCI) was embedded into LCS by the hot rolling technique. The macrostructure,
Learn MoreHeat Treatment in High Chromium White Cast Iron Ti Alloy
High chromium white iron is specially qualified for abrasion resistant applications. The predominant carbides in its structure provide it with a high hardness
Learn MoreMicrostructural modification of a static and dynamically
High-chromium white cast irons are ferrous alloys with Cr contents between 12 and 30% and 1.8–3.6% C. The as-cast microstructure is typically composed by a M7C3
Learn MoreMicrostructural and Erosive Wear Characteristics of a High Chromium
The present paper investigates the microstructural and erosive wear characteristics of a hypereutectic high-chromium cast iron, considering the erosion resistance, resulting from the impact of micro-sized particles, of both as-received and heat-treated conditions. Quezada, J.G.; Maldonado, C. Effect of titanium on the as-cast microstructure
Learn MorePDF Research Article Heat Treatment in High Chromium White Cast Iron Ti AlloyPDF
In the as-cast condition, the microstructure of high chromium molybdenum white iron consists essentially of dendrites of austenite in a matrix of eutectic mixture of austenite and (Fe, Cr)7C3carbides [ , ]. For many applications, castings are heat treated prior to service to increase the wear resistance as well as impact toughness.
Learn MoreMicrostructure and Sliding Wear Behavior of High Chromium Cast Iron
Microstructure and Sliding Wear Behavior of High Chromium Cast Iron Strengthened Low Carbon Steel Composite Abstract. To improve the wear resistance of the low carbon steel (LCS), high chromium cast iron (HCCI) was embedded into Introduction. Low carbon steel (LCS) is a widely applied material in
Learn MoreHot compression deformation and microstructure evolution of high
In this work, a canning compression process was developed to perform hot compression deformation of high chromium cast iron (HCCI) on a Gleeble 3800 thermomechanical simulator at temperature of 950-1150 °C and strain rate of 0.01 s -1. The hot deformation behavior and microstructure evolution of HCCI were investigated.
Learn More